Packaging Details

Inner packing: plastic bags  
Outer packing: Cartons,  
Pallet: Iron pallet,the iron pallet used in more suitable for customer

Port

Shanghai, Ningbo,Tianjing

Picture Example:

Primary Competitive Advantages:

1,Our company has sevals years’ experience in producing the copper fittings,we have the self-operated importing and exporting rights.
2,All products confirm strictly with ANSI/ASME B16.22 or EN1254-1.Our mould cover almost all of the American standard.
3,we can produce the copper fittings according to our customer’s requirment.and if their order quatities are big,we will not charge mould fee.
4,we can delivery the goods on time,prompt delivery if necessary customer required.
5,Small orders Accepted 

PhosCopper 2 is primarily used for the joining of copper-to-copper on vibration free joints.

It is very effective for joining tight-fitting copper pipe and tubing.

PhosCopper 2 should not be used on ferrous metals or copper alloys containing more than 10% nickel because of phosphorus embrittlement due to reactions with iron or nickel.

PhosCopper 2 has the ability to fill wide joint clearances at the lower end of its brazing range.

At the high end of the brazing range, it is more fluid.

Best results are obtained with clearances of 0.001-0.003″.

Melting of PhosCopper 2 is virtually complete at 1300°F (704°C).

Best results are obtained when brazing slightly above this temperature.

Generally, the joint strength produced by PhosCopper 2 will surpass the strengths of the base metals.

Strength is a function of the base metals being joined, type of joint, design of joint, joint clearances and brazing procedures.

The recommended maximum operating temperatures for PhosCopper 2 are 300°F (continuous service) and 400°F (intermittent service).

Corrosion resistance is satisfactory except when the joint is in contact with sulfurous atmosphere (especially at elevated temperatures).

The phosphorus content of PhosCopper 2 acts as fluxing agent, and no flux is necessary when brazing copper joints.

However, when used with a copper alloy or one of the other brazeable metals, White Silver Flux must be used to promote wetting, bonding, and flow throughout the joint.

The flow point of PhosCopper 2 is 1300°F (704°C).